- Material: Conventional and the HMLS (high modul...
- Place of Origin: Jiangsu China (Mainland)
- Supply Type: Make-to-Order
- Product Type: Other Fabric
Main specifications include: 1670dtex, 1440dtex, and 1100dtex, etc.
With adopting of advanced imported equipments, the dipped polyester tire cord fabric is characterized with such properties as high modulus, fatigue-proof and low shrinkage, etc., and thus becomes an ideal reinforcement material for high-performance semi-steel radial tires. Both types, the conventional and the HMLS (high modulus low shrinkage) are available for supply, with capacity of 6,000 t/a totally.
Main specifications include: 1670dtex, 1440dtex, and 1100dtex, etc.
Physical Properties of Dipped Conventional Polyester Tire Cord Fabric
Item | Unit | Specifications | |||
1100dtex/2 | 1440dtex/2 | 1670dtex/2 | |||
Break strength | N per end | ≥140.0 | ≥180.0 | ≥205.0 | |
EASL (elongation at specific load) | 44.1N | 4.5±1.0 |
|
| |
58.0N |
| 4.5±1.0 |
| ||
66.6N |
|
| 4.5±1.0 | ||
Elongation at break | 15.0±2.0 | 15.0±2.0 | 15.0±2.0 | ||
Adhesion (H-Test) | N/10cm | ≥125.0 | ≥130.0 | ≥140.0 | |
Coefficient of variation of break strength | ≤5.0 | ≤5.0 | ≤5.0 | ||
Coefficient of variation of elongation at break | ≤6.5 | ≤6.5 | ≤6.5 | ||
Dip pick up | 3.5±1.0 | 3.5±1.0 | 3.5±1.0 | ||
Cord gauge | mm | 0.56±0.03 | 0.61±0.03 | 0.66±0.03 | |
Twist number | Ply twist | T/m | 450±15 | 400±15 | 370±15 |
Cable twist | T/m | 450±15 | 400±15 | 370±15 | |
Thermal shrinkage | ≤3.5 | ≤3.5 | ≤3.5 | ||
Unpacking moisture | 1.0 | 1.0 | 1.0 | ||
Note:
1.For adhesion(H-Test) experiment, vulcanization condition: temperature(138±2), time 50min,pressure 3 MPa.
2.For thermal shrinkage test: temperature 177±2,time 2 min,load 0.05CN/dtex .
3.The above are the normal specifications and technical standards. If any special indices are requested in dimension stability, twist number, fabric width, warp and weft density, or roll length, etc., our company can tailor-make it for you.
Physical Properties of Dipped HMLS Polyester Tire Cord Fabric
Item | Unit | Specifications | |||
1100dtex/2 | 1440dtex/2 | 1670dtex/2 | |||
Break strength | N per end | ≥137.0 | ≥180.0 | ≥202.0 | |
EASL (elongation at specific load) | 44.1N | 4.5±1.0 |
|
| |
58.0N |
| 4.5±1.0 |
| ||
66.6N |
|
| 4.5±1.0 | ||
Elongation at break | 15.0±2.0 | 15.0±2.0 | 15.0±2.0 | ||
Adhesion (H-Test) | N/10cm | ≥125.0 | ≥130.0 | ≥140.0 | |
Coefficient of variation of break strength | ≤3.5 | ≤3.5 | ≤3.5 | ||
Coefficient of variation of elongation at break | ≤5.5 | ≤5.5 | ≤5.5 | ||
Dip pick up | 3.5±1.0 | 3.5±1.0 | 3.5±1.0 | ||
Cord gauge | mm | 0.56±0.03 | 0.61±0.03 | 0.66±0.03 | |
Twist number | Ply twist | T/m | 450±15 | 400±15 | 370±15 |
Cable twist | T/m | 450±15 | 400±15 | 370±15 | |
Thermal shrinkage | ≤2.0 | ≤2.0 | ≤2.0 | ||
Unpacking moisture | 1.0 | 1.0 | 1.0 | ||
Note:
1.For adhesion(H-Test) experiment, vulcanization condition: temperature(138±2), time 50min,pressure 3 MPa.
2.For thermal shrinkage test: temperature 177±2,time 2 min,load 0.05CN/dtex .
3.The above are the normal specifications and technical standards. If any special indices are requested in dimension stability, twist number, fabric width, warp and weft density, or roll length, etc., our company can tailor-make it for you.